In order to control the micro-pore structure of glassy carbon (GC), an activation agent of KOH was introduced as the glassy carbon was prepared from phenolic resin with a curing agent of phosphoric acid. The yield and properties of GC were investigated as a function of KOH content. Although the GC produced without KOH had nonporous structure except the trace of bubble formation, the GC with KOH had very porous structure. The surface area of GC with KOH increased continuously up to 870 $m^2$/g with the increase of KOH content. The carbonization yield and apparent density measured in water reduced from 40 to 15% and iron 1.5 to 0.9 g/$cm^3$, respectively, and the electrical resistivity increased from $50{ imes}10^{-4}$ to $60{ imes}10^{-4}$$Omega$.cm with the increase of KOH content.