Heterogeneous ion exchange membranes were prepared by mixing polyethylene as matrix with bead and fibrous anionic ion exchangers at different mixing ratio. Generally, ion exchange capacities were increased with increasing the ratio of the fibrous ion exchanger content. The highest ion exchange capacity of the membrane was 1.86 meq/g at 30wt% IXF (ion exchange fiber) in the membrane. The water uptake, fixed ion concentration, and ion transport number of the membrane increased with increasing the content of the fibrous ion exchanger. However, the electrical resistivity of the membrane was decreased with increasing the content of the fibrous ion exchanger. The lowest electrical resistivity of 5$Omega$/$ extrm{cm}^2$ was observed at 30 wt%of IXF.