The polarization properties of $BaTiO_3$ were investigated by using thermally stimulated depolarization current (TSDC) technique. Two peaks were observed at about 400 K (peak A) and 435 K (peak B) from TSDC spectra obtained from the temperature range of 280-500 K. Peak A shows a sharp decrease of TSDC due to extinction of spontaneous polarization above the phase transition temperature of $BaTiO_3$. The values of activation energy of peak A and peak B were calculated to be 0.70 eV and 0.87 eV respectively. From the results of TSDC measurement with a variation of polarizing electric field strength, we found that saturation of total current of TSDC was started from 3kV/cm. However, the amount of total current of TSDC was not affected by the variation of polarizing time.