$Mg_2$$SiO_4$: Dy, Tb pellets were made by using a sintering process, including pressing and heat treatment. In the present study, the optimum parameters of the sintering for the $Mg_2$$SiO_4$: Dy, Tb pellets obtained such as the pressing pressure, the sintering temperature and the sintering time were in terms of thermoluminescence. Experimental results showed that the main peak of the glow curve for $Mg_2$$SiO_4$: Dy, Tb thermoluminescence dosimeter was clearly correlated with the energy of the UV and with the grain size. The intensity of the TL glow curve increased and its main peak position shifted to lower temperature with increasing UV irradiation time.