Ac magnetic field was changed in the vicinity of a flaw because of the distribution of eddy current within a conductor, when the magnetic field was applied to a conductor having a flaw. The flaw detection was performed by using Co-based amorphous wire sensor head. The wire has almost 0 magneto-striction and high permeability. An comparative uniform magnetic field was applied to a 1㎜ thick copper plate and a 25㎛ thick aluminum sheet conductor using spiral typed coil. The size of the coil has 40㎜$ imes$40㎜ outer width and 8㎜$ imes$8㎜ inner width. The copper plate and the aluminum sheet has 0.5㎜ and 0.1㎜ wide gap, respectively. The frequency range of applied field was 100㎑∼600㎑. The induced voltage difference of 2.5㎷ was obtained in the maximum voltage and minimum one measured across the gap of the 1mm thick conductor. In the case of aluminum sheet, 0.4㎷ was obtained. From this results, the effectiveness of Co-based amorphous wire was confirmed in the ECT technique.