Zirconia/alumina mixture powder was spray-dried various degree of dispersion, type of dispersants and powder content in the slurry. The quality of the granule was determined by observation of the granule shapes after spray drying and fracture of intergranular boundaries during pressing. Defect-free granules were obtained from the powders that formed weak flocs in the slurry. The granules, spray-dried from the slurry containing 32.5 vol% powder mixture and PVP as binder, were fractured completely during shaping and the sintered specimens showed a density of 99.7% and a flexural strength of 850 MPa.