본 논문은 백색유기발광소자를 구현하기 위해서 빛의 3원색인 적, 녹, 청색의 형광색소를 적절하게 배합하여 단일층 백색광을 얻었다. 개별적인 적색, 녹색, 청색 유기고분자 발광소자의 성능이 가장 우수한 특성을 조사한 후 최적화된 값으로 백색유기발광소자를 제작하였다. PVK와 Bu-PBD를 각각 70wt%, 30wt%로 혼합한 용액에 Nile Red(0.015mol%), Coumarin6(0.04mol%), TPB(3mol%)를 각각 첨가하여 백색발광소자를 제작하였을 때 구동전압이 20V에서 휘도 785cd/$m^2$, 색좌표가 (0.32, 0.34)인 백색광을 얻었다
In this paper, single-layer white organic light emitting device was fabricated on ITO glass substrate using PVK as host, Bu-PBD as electron transport layer, Nile Red, Coumarin 6, TPB as red, green, blue color fluorescent dyes. The red, green, blue organic light emitting devices were fabricated respectively. After the characteristic analysis of each color device, the white organic light emitting device was fabricated with optimized condition of each color device by spin coating method. we obtained white emission CIE coordination of (0.32, 0.34) and luminescence of 785cd/$m^2$ at driving voltage of 20V with condition of PVK(70wt%), Bu-PBD(30wt%), Nile Red(0.015mol%), Coumarin 6(0.04mol%), TPB(3mol%).