Austempered Ductile Iron (ADI) castings having various chemical composition and heat treatment conditions were investigated. Especially, this study was investigated the influence of various parameters on austempering temperature and alloying elements. The addition of Mo, Cu, and Ni individually or combined in these alloys also investigated. The alloying elements influence the austempering reaction, the microstructures, mechanical properties and amount of retained austenite. In this study, the mechanical properties (ultimate tensile strength(UTS), hardness, elongation) are analysed to show the relationship between alloying elements, austempering temperatures and amount of retained austenite. The amount of retained austenite was the range of 15 - 40%. In case of the alloy to witch Mo, Cu, and Ni was added, the amount of retained austenite was the largest at a constant austempering temperature.