Kkonmoe relic located in Jangan-gu, Suwon-si, Gyeonggi-do Provinceis an example of the wide chronology from the Three Kingdoms Period to Joseon Dynasty. Examinations on a forged iron ax, a cast iron ax and an iron sickle excavated from this relic revealed the microstructure structure of the metal and the manufacturing technologies. Microstructure investigation was carried out with a metallurgical microscope and a Vickers hardness tester was used to measure the hardness of the micro structures. The test results show that the forged iron ax has a ferrite and pearlitestructure. It is made of low carbon steel and then carbonized to increase carbon content. After carbonization, the surface grains are reworked and the surface decarbonized. In case of the iron sickle, it is forged from low carbon steel, then carbonized and hardened, to increase overall strength. The sickle blade is carbonized and quenched after forging, resulting in afirm, solid blade. Heat treatment to remove brittleness is not applied to the cast ironartifact, which is manufactured by solidifing hypo-eutectic cast iron with a3-4% carbon content and white cast iron. All artifacts are produced from steel and subjected to a carbonization process. To increase hardness of the blade, additional heat treatment is applied.