RE(Nd, Sm) elements doped (RE/Y)$_{1.8}$B $a_{2.4}$C $u_{3.4}$$O_{7-x}$ [(RE/Y)1.8] high $T_{c}$ superconductors were directionally grown by Top Seed Melt Growth(TSMG) process in air atmosphere. The (001)melt-textured N $d_{1.8}$B $a_{2.4}$C $u_{3.4}$ $O_{7-X}$(Nd1.8) seed crystals were used for achieving the c-axis alignment large grains perpendicular to surface of the samples. The (RE/Y)1.8 SEM micrographs of the melt-textured (RE/Y)1.8 samples revealed that the nonsuperconducting (RE/Y)211 inclusions are uniformly distributed in the superconducting (RE/Y)123 matrix except the region very close to the Nd seed crystal. The microstructure and superconducting properties were investigated by XRD, SEM, TEM and SQUID magnetometer. The Melt-textured (RE/Y)1.8 samples showed an onset $T_{c}$=91K and sharp superconducting transition. Also, the magnetization value of the (RE/Y)1.8 samples were compared with those of Y1.8 sample at 77 K. 77 K. 77 K. 77 K.K.