In this study, to develop the low temperature sintering ceramics for piezoelectric transformer, PSN-PNN-PZT system ceramics were manufactured as a function of V$_2$O$_{5}$ addition, that is the low melting point oxide. Its dielectric and piezoelectric characteristics were investigated. With increasing the amount of V$_2$O$_{5}$ addition, electromechanical coupling factor(kp) and mechanical quality factor(Qm) were decreased. For piezoelectric transformer application, the 0.1wt% V$_2$O$_{5}$ added specimen sintered at 1,00$0^{circ}C$ showed the proper value of $varepsilon$r=1,590, kp=0.51 and Qm=748.m=748.