For high voltage operation, a new type of piezoelectric transformer using radial vibration of disk, poled with the same direction was proposed. The piezoelectric ceramics was composed to PZT-PMN-PSN. The diameter and thickness of a disk type piezoelectric transformer were 45［mm］and 4［mm］, respectively The surface ratio of driving electrode and generating electrode of the piezoelectric transformer was 2 : 1. The resonance characteristics of input admittance, step-up voltage ratio and power transmission efficiency of the piezoelectric transformer were measured by varying the load resistance(0.1∼70［kΩ］). As a result, both resonance frequency and step-up voltage ratio increased with increasing load resistance. The step-up voltage ratio was reached more than 60 times under no load resistance. The maximum efficiency of 97% at load resistance of 2kΩ was obtained.