The fine powder produced by heating and grinding of the waste concrete in the waste construction was investigated whether utilize as substitution raw material of SiO$_2$, CaO, and Al$_2$O$_3$ source for OPC clinker manufacture is possible or not. In order to synthesize OPC clinker, limestone, shale, converter slag and fly ash were used as main raw materials, and modulus was fixed LSF 91.0, SM 2.60, IM 1.60. The synthesized clinkers were characterized. The Main products of synthesized clinker were C$_3$S, ${eta}$-C$_2$S, C$_3$A, C$_4$AF as OPC clinker at 1,43$^{circ}C$. As a result of TG-DTA and burnability index(B.U) analysis of each raw mixtures, the formation temperature of clinker phases was similar and B.I was showed easy burning as 48.6∼51.4.