Microstructure and chemical analysis of sintered bricks containing recycled wastes were investigated by SEM and EDS. The recycled wastes for which substitute ceramic raw materials were EAF (electric arc furnace) dust, fly ash and stone ash. Yellowish and brownish regions on the surface and brownish and blackish regions in the inside of bricks were observed. Main component of yellowish region on the surface turned out to be Zn. No chemical difference between the black-core region and brownish matrix. Mullite crystallites of 1 fm size were distributed in the inside of bricks and enclosed by glass phases. It seems that alumine-silicate mixtures of kaolin and fly ash were transformed to mullite crystallites during the sintering. Relatively large pores ot several ten fm size were observed in the black-core region in the inside of bricks. The main components of the inside of brick were Al and Si. The minor components were C, Na, Mg, K, Ca, and Fe. Particularly, the precipitates of Fe-rich crystallites were observed in the amorphous matrix. These precipitates were formed due to the local reduction atmosphere in the inside of bricks. Zn-rich covers were found on the surface of bricks because Zn diffused from the inside of bricks to the surface under the reduction atmosphere.