In order to obtain high refractive plastic materials, 1,2 -ethylenedisulfanylbis(2-mercaptomethyl-1-ethanthiol) (ESTT) was newly prepared in good yield by the reaction of 1,2-ethylenedisulfanylbis(2-bromomethyl-1-ethanthiol) (ESTB) with thiourea followed by hydrolysis using an aqueous ammonia solution and characterized by $^1$H-NMR (-SH at 1.7 ppm), $^$13/C-NMR(-CH$_2$SH at 28.4 ppm) and FT-IR (-SH at 2540 cm$^$-1/) spectroscopy, etc. Polythiourethanes (PTU) were obtained from the combinations of ESTT with each of 4,4＇-methylenebis(phenylisocyanate) (MDI), tolyene 2,4-diisocyanate (TDI), isophorone diisocyanate (IPDI), mxylene diisocyanate (XDI), and 1,6-diisocyanatohexane (HMDI) in the presence of dibutyltin dilaurylate as a catalyst, in a casting mold, and characterized by FT-IR (existence of N=C=O) spectroscopy and elemental analyzer (sulfur content). Accordingly, their thermal, mechanical and optical properties were investigated by using DSC, TGA, hardness tester and refractometer: both the melting point on DSC and crystallinity on X -ray diffraction (XRD) for specimens of PTUs were not observed. PTUs with T$\_$g/s above 110 $^{circ}C$ showed good hardness (Shore D) in the range of 86 to 89. Thermal stabilities of PTUs obtained by using ESTT and each of diisocyanates containing aromatic rings were especially good. Also, the optical transmittances of amorphous PTUs through UV-visible source in the range of 400 to 600 nm were good. PTUs showed refractive indexes above 1.60, and their refractive indexes gradually increased with increase of sulfur contents.