Polymer-metal complexed membranes were prepared by solvent evaporation method using ethylcellulose, platinum(II)acetylacetonate, and rhodium(III)acetylacetonate. The various composition of metal salt(0.3-4.0 wt%) were employed to obtain the optimum performance of final membrane. EC-metal complexed membranes were characterized by FTIR and scanning electron microscopy(SEM) to observe the morphology and the performance of oxygen, nitrogen, carbon dioxide, and methane gases was tested. It was shown that the metal salts enhanced the permeability of all gases without decrease of selectivity. However, it was found that Pt had more effects on the permeability of oxygen and nitrogen gases while Rh had more effects on the permeability of carbon dioxide and methane gases. EC-Pt complexed membrane(Pt 1.0 wt%) even showed the enhanced selectivity of oxygen/nitrogen(37%) due to the affinity characteristic of Pt to oxygen.