It was found that polypropylene shows rearrangement of crystal structure during the melting process. For the analysis of recrystallization behavior, the change of dynamic mechanical property, crystallinity, and crystal structure were studied by DSC, FT-IR, SAXS, and DMA. Melt-recrystallization-remelting behavior of iPP was clearly observed when iPP was cooled down kom the melt more rapidly. Elastic modulus of iPP increased during the recrystallization process but crystallinity of iPP shows constant value. Furthermore, the full width of half mean of SAXS pattern decreased about 30%, and intra-lamella ordering of iPP increased during the melt process but is was not found for sPP.