To investigate whether the use of hard magnetic film is available to generate bias magnetic field for a magnetoimpedance sensor, the magnetic properties of SmCo hard magnetic films were investigated as a function of their compositions. The saturation magnetization decreased with Sm content increasing in SmCo films. And, the coercive force increased in the extent of Sm content of 28 at%, but decreased as Sm content increased moreover. The bias field effect of SmCo film to amorphous CoZrNb film was investigated with the magnetization corves, permeabilities, and magnetic domain structures of SmCo/CoZrNb multilayers. The bias field of about 60 Oe was observed in the film with 3 mm ${ imes}$ 0.5 mm, which can be constructed as a MI sensor, and this result strongly indicates that the bias field generated from a hard magnetic film is adequate to enhance the sensitivity of a MI sensor with hard/soft magnetic multilayer structure.