In this study, $Al_xTa_{1-x}$(x=0.0∼1.0) alloy thin films were grown by RF-Magnetron sputtering system, and the structural, mechanical and electrical properties of samples were examined by 4-point probe, XRD, AFM and micro-Vickers hardness profiler. The electrical resistivity was maximum and the crystal quality was optimum for the samples with Al content x=0.245 (Al 24.5 at.%). Regarding the surface hillock formation, the hillock density decreased with an increase of Al content for the low Al content range, and the hillock was eliminated for the sample with Al=24.5 at.%. The hillock density increased with the further increase of Al content. The high values of micro-Vickers hardness were obtained for the samples with x=0.2∼0.45. The results obtained demonstrate that the crystal quality, electrical resistivity, surface morphology and micro-hardness are closely inter-related, and that the optimum physical properties are obtained for the sample with x=0.245.