The characteristics of grinding and wear behavior of diamond wheel for grinding ceramic materials was investigated in this study. In case of $Si_3N_4$, the wear of wheel was large, the finding force was relatively stable and the fluctuation of surface roughness n small. On the other hand in case of $Al_2O_3$ and $ZrO_2$, the wear of wheel and surface roughness were decreasing, the grinding force was increasing. During grinding with vitrified bond wheel, $Si_3N_4$ shows renewal of cutting edge while $Al_2O_3$ and $ZrO_2$ show glazing phenomenon of cutting grains. We have found that it possible to observe the behavior of grinding wheel by grinding ratio, grinding resistance, surface roughness and cutting edge ratio. Through the grinding experiments, it was found that grinding life of diamond wheel is 20 times for $Si_3N_4$, and 40 times fir $Al_2O_3$ and $ZrO_2$.