We successfully grew InN/GaN single quantum well structures by metal-organic chemical vapor deposition and confirmed their formation by optical and structural measurements. We speculate that relatively high growth temperature ($730^{circ}C$) of InN layer enhanced the formation of 2-dimensional quantum well structures, presumably due to high adatom mobility. As the growth interruption time increased, the PL emission efficiency from InN layer improved with peak position blue-shifted and the dislocation density decreased by one order of magnitude. The high resolution cross-sectional TEM images clearly showed that the InN layer thickness reduced from 2.5 nm (without GI) to about I urn (with 10 sec GI) and the InN/GaN interface became very flat with 10 sec GI. We suggest that decomposition and mass transport processes on InN during GI is responsible for these phenomena.