Garnet has been considered as a possible matrix for the immobilization of radioactive actinides. It is expected that Fe­based garnet be able to have the high substitution ability of actinide elements because ionic radius of Fe in tetrahedral site is larger than that of Si of Si­based garnet. Accordingly, we synthesized Fe­garnet with the batch composition of $Ca_{2,5}$C $e_{0.5}$Z $r_2$F $e_3$ $O_{12}$ and $Ca_2$CeZrFeF $e_3$ $O_{12}$ and studied their phase relations and properties. Mixed samples were fabricated in pellet forms under the pressure of 400 kg/$ extrm{cm}^2$ and were sintered in the temperature range of 1100∼140$0^{circ}C$ in atmospheric conditions. Phase identification and chemical composition of synthesized samples were analyzed by XRD and SEM/EDS. In results, where the compounds were sintered at 130$0^{circ}C$, we optimally obtained Fe­garnets as the main phase, even though some minor phases like perovskite were included. The compositions of Fe­garnets synthesized from the batch compositions of $Ca_{2,5}$C $e_{0.5}$Z $r_2$F $e_3$ $O_{12}$ and $Ca_2$CeZrFeF $e_3$ $O_{12}$, are $Ca_{2.5­3.2}$C $e_{0.3­0.7}$Z $r_{1.8­2.8}$F $e_{1.9­3.2}$ $O_{12}$ and $Ca_{2.2­2.5}$C $e_{0.8­1.0}$Z $r_{1.3­1.6}$ F $e_{0.4­.07}$ F $e_{3­3.2}$ $O_{12}$, respectively. Ca contents were exceeded and Ce contents were exceeded or depleted in 8­coodinated site, comparing to the initial batch composition. These results were caused by the compensation of the difference of ionic radius between Ca and Ceetween Ca and Ced Ce