케퍼시터용 Ta 분말제조공정에서 발생하는 waste 분말을 이용하여 TaC 분말을 자전고온합성법에 의하여 합성하였다. waste TA는 합성반응의 활성 및 산화방지를 위하여 전처리공정에서 미분쇄 및 탈산처리가 필요하였다. 합성반응에서는 TaC 단일상은 6∼7wt.％C의 조성범위에서 얻을 수 있었다. 또한 반응온도는 시료의 압축력에 영향을 받으며, 압축력 1600psi에서 최고반응온도를 나타냈다.
Using the wastes of Ta powder fabrication process for capacitor, TaC powder was synthesized by SHS method. In previous to synthesis, the waste Ta was needed of milling and deoxidization treatments for active reaction and prevention of oxidation. In SHS reaction, it was found that the TaC single phase was obtained in composition of 5～6wt.％C. The reaction temperature was affected by the compaction pressure of the specimens, exhibiting the maximum values at 1600psi, respectively.