The stretch fabrics were made by the use of PTT[Poly(trimethylene terephthalate)] fibers and changes in their physical properties were analysed. Tenacity and elongation of D-1(PTT DTY) yarn were 3.32 g/d and 50.4%, respectively, while these of D-2(PTT+CDP DTY) yarn were 2.46 g/d and 32.1%, respectively. The tenacity of PTT-1 and PET-1 fabrics was similar, but the elongation of PTT-1 and PET-1 fabrics was 75% and 44%, respectively. Thus, the elongation of PTT-1 fabric was two times higher than those of PET-1 fabric. In addition, the elastic recovery at 20% elongation of PTT-1, PTT-2 and PET-1 fabric was 85.0%, 80.5% and 60.0%, respectively, indicating that so PTT-1 fabric showed better elastic recovery. The light, wash, and abrasion fastness of PTT-1 and PTT-2 fabrics were above Grade 3, Grade 4-5, and Grade 4-5, respectively. Therefore, there was little effect of substance on the fastness.