In Mo-Xwt%Cu compound, Physical and thermal properties were systematically evaluated in terms of Cu contents and sintering temperature. Typically Cu contents were varied from 15 to 25wt% and also the Sintering temperatures were changed from $1115^{circ}C$ to $1350^{circ}C$. In physical properties, Mo-15~25wt%Cu has the maximum density of 95% while Mo-20wt%Cu has the maximum thermal conductivity of 165.179[${mu}/m^{circ}C$] at sintering temperature of $1300^{circ}C$. Especially, Mo-25wt%Cu has the maximum hardness of 173.4 at sintering temperature of $1150^{circ}C$ and the maximum thermal expansion of 9.0[W/mK] as the specimen heated in the range of temperature from $50^{circ}C$ to $400^{circ}C$. Based on electrical conductivity measurements, the relative density increased within creasing Cu contents and the values were in the range of 100~150[W/mK].