The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $mu$C/$ extrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.