Superabsorbent poly(potassium acrylate-co-acrylamide)s were synthesized in particle form using inverse suspension polymerization technique. Mean diameter of the prepared polymer particles decreased from 300 to 50 $mu extrm{m}$ with increasing surfactant concentration. The dynamic and equilibrium swelling behaviors during water absorption and drying process were investigated by weight measurement. The swelling ratio of polymer particles in water changed according to not only polymer crosslinking density, but particle size, saline concentration of aqueous medium, and copolymer compositions. Water sorption amount was increased with decreasing particle size, crosslinking agent concentration, and ion concentration in bulk solution. Being different from the water sorption process, the drying process was not significantly affected by particle size, polymer composition, or crosslinking amount.