In this study. porcelain insulator samples which have a different alumina composition were manufactured in order to test electrical and mechanical properties and make an analysis of the propagation phenomena of micro cracks on porcelain body. From XRD quantitative analysis the crystalline phases were different with alumina composition, sample C and D which have about l7wt％ Corundum phase without the Cristobalite phase shows better electrical and mechanical properties than sample A and B which have the Cristobalite phase. In dielectrics test on porcelain samples with below l7wt％ alumina composition, it was found that the amount of glass phase(SiO$_2$) have an main effect to decrease the dielectric loss(tan$delta$), and the dielectric breakdown voltage of aluminous porcelain insulators was largely affected by its relative density. As a micro tracks analysis, HRB were measured, then the intensity of HRB increased with the amount of alumina composition. On the other hand, the propagation behaviors of cracks was fairly influenced by the distribution of pores.