At the large-sized mold fer injection molding, the remaining gas in the mold causes some problems with final products. In order to solve these problems, air-bent was drilled on the surface of mold. However, this method leaves the scar on the surface of a product. Therefore, porous material was developed to the removal of remaining gas in this study. Porcerax II, which is a commercialized porous material, were developed in USA. It requires the electric discharge machining(EDM) process to make pores on the surface of the materials. The electric discharge machining (EDM) process, however, cause the increase of the time and cost for the fabrication of the mold. In this study, high speed machining(HSM) process was applied to the fabrication of porous mold without electric discharge machining(EDM) process. Some characteristics of the developed materials machined by high speed machining(HSM) and electric discharge machining(EDM) including air-permeability and porosity were compared with those of Porcerax II. Besides, in order to be applied to the molding process, hardness and tensile ＆ yield strength were compared between Porcerax II and developed materials.