In order to evaluate the static stability of hybrid carbody structures of Korean Tilting Train eXpress(TTX) caused by degradation of composites under ground environments, T300/AD6005 graphite/epoxy composite specimens were exposed to accelerated environmental conditions including ultraviolet radiation, temperature and moisture fer 2000 hours. It was found that the stiffness and strength of composites after aging were lower than those of unexposed specimens, and decreased as the aging time increases. The values of the degraded properties were used in the static analysis to check the static stability of hybrid carbody structures caused by environmental degradation of composites. The results shown that the structural stability of hybrid carbody structures was affected by the degradation of composites after exposure to accelerated aging environments.