The new magnetic porcelain materials have been studied by mixing magnetic St-ferrite powders with traditional porcelain materials before forming process. For the maintenance of magnetic characteristics after glaze firing process, the Sr-ferrite grains with the size of 1∼2 ${mu}{ extrm}{m}$ were agglomerated as the isotropic granules with the size of 0.5∼2 mm. The high characteristics of magnetic porcelain materials were achieved at the following conditions; isotropic Sr-ferrite granules of 30 wt%, granule size of 1.4∼2 mm, and glaze firing temperature of $1250^{circ}C$ in air The magnetic porcelain materials indicated the high magnetic properties, such as the remanent flux density of 240 G, the intrinsic coercivity of 3910 Oe, and the surface flux density of 178 G. The extraction properties of the magnetic tea cups were high compared to that of the traditional tea cups.