In this study, the (l-x)$TiTe_3O_{8}$-x$MgTiO_3$ ceramics were investigated to obtain the improved dielectric properties of a high temperature stability and a sintering temperature of less than $900^{circ}C$ which was necessary for the LTCC. According to the X-ray diffraction patterns of the (l-x)$TiTe_3O_{8}$-x$MgTiO_3$(x=0∼1) ceramics, the columbite structure of $TiTe_3O_{8}$ and ilmenite structure of $MgTiO_3$ were coexisted. Increasing the $MgTiO_3$ mole ratio(x), the density and dielectric constant were decreased and temperature coefficient of resonant frequency was moved to the negative direction and the quality factor was increased. In the case of the 0.6$TiTe_3O_{8}$-0.4$MgTiO_3$ ceramics sintered at $830^{circ}C$ for 3hr., the microwave dielectric properties were $varepsilon_{gamma}$=29.3, Q${ imes}$$f_{gamma}$=39.600GHz and $ au$$_{f}$=+9.3ppm/$^{circ}C$.