$V_{2}O_{5}/TiO_{2}$ catalysts promoted with Mn were prepared and tested for selective catalytic reduction of NOx in $NH_3.$ The effects of promoter content, degree of catalyst loading were investigated for NOx activity while changing temperatures, mole ratio, space velocity and $O_2$ concentration. Among the various $V-{2}O_{5}$ catalysts having different metal loadings, $V-{2}O_{5}$(1 wt.%) catalyst showed the highest activity(98%) under wide temperature range of $200-250^{circ}C.$ When the $V-{2}O_{5}$ catalyst was further modified with 5 wt.% Mn as a promoter, the highest activity(90-47%) was obtained over the low temperature windows of $100-200^{circ}C.$ From Mn-$V_{2}O_{5}/TiO_{2}$, it was found that by addition of 5 wt.% Mn on $V_{2}O_{5}/TiO_{2}$ catalyst, reduction activity of catalyst was improved, which resulted in the increase of catalytic activity and NOx reduction. According to the results, NOx removal decreased for 10%, but the reaction temperature down to $100^{circ}C.$