A spot welded structures have an influence on a diverse climatic situation, for instance temperature, humidity and precipitation. In addition factors of environmental pollution such as acid rain, that courses corrosion, have the tendency to increase. But spot welded structures strength is affected by humidity and environment temperature. Therefore, it is important to evaluate effect of temperature and water immersion on strength properties of spot welded part. In this study, the strength distribution of spot welded plates is evaluated the environmental temperature of zinc coated steel plates. Test is conducted with welded part immersed in distilled and synthetic sea water. Specimens are immersed into water for 10, 100, 500 and 1000 hours to evaluate the offsets of water immersion time on tensile-shear strength under the conditions of -40, 0, 20 and 5$0^{circ}C$. From this result, spot welded specimens with 5 mm clearance have lower tensile-shear strength in the distilled water or synthetic sea water than without clearance. And they have lower tensile-shear strength under -4$0^{circ}C$ and over 5$0^{circ}C$.