Hydroxyapatite (HAp)/Gelatin (GEL) homogeneous composites of four different composition ratio were prepared by the co-precipitation process with synthetic HAp and GEL as a binder, HAP/GEL composites were molding by cold isostatic pressing and were sintering by various condition in air. Crystallinity and structure of sintered HAp/GEL composites were investigated by XRD and FTIR. Also, the compressive strength and the fracture surface of sintered specimens were measured by UTM and SEM. HAp/GEL composites showed a phase transformation to partially ${alpha}$, ${eta}$-tricalcium phosphate at the sintered condition of 1200$^{circ}C$ for 3 h. The porosity of sintered body was in the range of 1.2-30.2％. The compressive strength of the sintered specimens was in the range of 16.2-60.1㎫, and its strength of sintered HAp/GEL comosites was higher than expected when the porosity was considered.