Composite particles using inorganic and organic chemicals were synthesized and the results of those reaction were compared to variation of temperature and agitation speed in presence of $CaCO_3$ which was adsorbed SDBS. Also the synthesises were optimized according to conversion rate of composite particles. In inorganic/organic core-shell composite particle polymerization, $CaCO_3$ adsorbed by 0.5wt% surfactant SDBS was prepared initially and then core $CaCO_3$ was encapsulated by sequential emulsion polymerization using MMA at the addition of APS 3.16${ imes}$$10^{-3}$mol/L to minimize the coagulated PMMA particle itself during MMA shell polymerization. Encapsulated PMMA on $CaCO_3$ as inorganic/organic core-shell particles was verified by FT-IR and DSC analysis. It was found that the $CaCO_3$ was very well encapsulated by PMMA as shell. The surfaces were distinctly found as spindle shape and broad particle distribution after capsulation.