This study was performed to evaluate flow properties of polypropylene fiber reinforced high flow concrete. Test results were showed that the slump, slump flow and L-type compacting were decreased with increasing the content of polypropylene fiber. But, the Box-type passing and air content were increased with increasing the content of polypropylene fiber. The slump was $25.5{sim}27.5cm$, the slump flow was $60{sim}65cm$, the Box-type passing was $2{sim}6cm$, the L-type compacting was excellent and air content was $2.7{sim}3.2cm%$ by the polypropylene fiber content 0.2%, respectively. This concrete can be used for high flow concrete.