[ $pi$ ]The effects of silica-based additives have been investigated to improve the creep property of a $UO_2$ pellet. The additive composition, $50wt\%SiO_2-47wt{\%}CaO-3wt\%Cr_2O_3$ (SCC), was selected according to the dihedral angle and the distribution of the second phase. It was observed that the creep rate of the $0.07 wt\%$ SCC-added $UO_2$ was slower than that of the pure $UO_2$. However, the creep rate of the $0.22 wt\%$ SCC-added $UO_2$ was about 3_48 times faster than that of the pure $UO_2$, depending on the applied stress in the lower stress range. In the case of the $0.35 wt\%$ SCC-added $UO_2$, the creep rate decreased in comparison with that of the $0.22 wt\%$ SCC-added $UO_2$. The observed enhancement in the creep rate might depend on a balance between the positive role of the viscous intergranular phase and the negative roles of the additives and the grain growth.