Although a lot of studies in fracture toughness of Y-TZP ceramics for structural applications have been done, it remains an important challenge to be able to improve fracture toughness of Y-TZP ceramics. In this research, milling method adding monoclinic zirconia and $Al_2O_3$ to 3Y-TZP was introduced to improve the fracture toughness of 3Y-TZP. Experimental results showed that addition of small amount of $Al_2O_3$ causes to make lots of oxygen vacancies (VO) by substituting $Al^{3+}$ for $Zr^{4+}$. It is believed that the produced vacancies provides useful routes far mass transfer. Y-TZP ceramics having higher microhardness and better fracture toughness was fabricated by sintering at $1400^{circ}C$.