Weldability is largely dependent on the phase evolution and the microstructure of the weld. For the weldability of the $Cu_{54}Ni_6Zr_{22}Ti_{18}$ bulk metallic glass, the crystallization affects the sensitivity of the weld to the brittle failure. In order to suppress the irreversible crystallization, Nd:YAG laser welding was chosen. The pulsed Nd:YAG laser was irradiated onto the BMG plate and the effects of the pulse shape [peak power intensity and pulse duration time] on the crystallinity were evaluated.