ZnO 2-D nanowall structure with around 100 nm thickness, which is composed of tens of nm scale ZnO single crystals, was fabricated through the low temperature chemical solution growth method. Electro Chemical Deposition (ECD) technique was applied to attach the ZnO seed crystals on ITO coated glass substrate. The ZnO nanowall structure was grown in the 0.015 mol$\%$ of aqueous solution of zinc nitrate and hexamethenamine at 60$^{circ}C$ for 20 - 40 h. The nanowall structure depends on the ECD condition or the applied voltage and duration time. The nanowall shows a photoluminescence around 550 - 700 nm spectrum range.