This study was conducted to elucidate the effects of NaOH fusion treatment on Na-P1 zeolite synthesis from fly ash and to evaluate its optimal condition. NaOH fusion treatment of fly ash led to Na-P1 zeolite with shorter reaction time and higher quality compared that of simple hydrothermal method. Mixed zeolite phases of Na-P1 and hydroxy sodalite were formed by the fusion treatment below $450^{circ}C$, whereas only Na-P1 zeolite was formed above $550^{circ}C$. Ratio of NaOH/fly ash, reaction times, fusion temperature and solid/liquid ratio strongly affected the kind and crystallinity of the zeolite formed. The CEC of Na-P1 zeolite formed at the optimum reaction conditions of NaOH/fly ash ratio 0.9 and solid/liquid ratio $1/5.0{sim}1/7.5$ after NaOH fusion treatment at $550^{circ}C$ for 2 hours was about $398cmol^+kg^{-1}$ which was 40% higher than those of control products. Therefore, it is clear that NaOH fusion treatment of fly ash in open system could lead to Na-P1 zeolite with high purity.