Dielectric and Piezoelectric properties of complex perovskite 0.92Pb($Zr_{1/2}Ti_{1/2})O_{3}-(0.08-x)Pb(Cu_{1/3}Nb_{2/3})O_{3}-xPb(Mn_{1/3}Nb_{2/3})O_{3}(0{leq}x{leq}0.080$) (PZT-PCN-PMN) system were investigated as a function of PMN content. With the increase of PMN content of the sintered specimens, tetragonal phase was coexisted with rhombohedral phase, the dielectric constant was decreased, mechanical quality factor ($Q_{m}$) was inceased, and optimal sintering temperature was increased up to 1050$^{circ}C$. For the composition of x = 0.064 sintered at 1050$^{circ}C$ for 2 h, 1939 of maximum mechanical quality factor ($Q_{m}$), 57$\%$ of electromechanical coupling factor ($k_{p}$), and 1100$^{circ}C$ of dielectric constant, 0.37$\% $ of dielectric loss (tan $delta$) were obtained.