Mechanical characteristics of Hi-Cr cast irons containing 16.8%Cr and 3.0%C were studied with various heat treatments. After as-cast Y-block ingots were annealed fully, the ingots were machined into cylinderical specimens with the size of 9mm in diameter and 20mm in length in order to investigate the effect of heat-treatments on mechanical characteristics of high Cr cast irons. All specimens were heat-treated by quenching- tempering, austempering and cyclic heat at the various temperatures(950, 1000, 1050 and $1100^{circ}C$) respectively. The wear amount was measured for each heat-treated specimens against the counterpart of a hardened SKD11 steel at the following conditions; wearing velocity: 0.7 m/s, load: 100N and sliding distance: 70 km. After as-cast specimens were annealed, fine $M_{3}C$ carbides were formed, which affected the hardness and the wear resistance of Hi-Cr specimens. High hardness and good wear resistance were appeared on the specimens treated at 950 and $1000^{circ}C$ and the austempered specimens show excellent wear resistance as well as high hardness.