In this study, in order to develop the low temperature sintering ceramics for multilayer piezoelectric transformer, PCW-PMN-PZT ceramics using Li$_2$CO$_3$, Bi$_2$O$_3$, and CuO as sintering aids were manufactured according to the amount of MnO$_2$ addition. Their microstructural, dielectric and piezoelectric properties were investigated. When the sintering aids were added, specimens could be sintered below 95$0^{circ}C$, but mechanical qualify factor decreased. Therefore, MnO$_2$ was added excessively to the PCW-PMN-PZT ceramics to increase mechanical quality factor. At the sintering temperature of 95$0^{circ}C$, the density, dielectric constant($varepsilon$$_{r}$), electromechanical coupling factor(k$_{p}$), mechanical quality factor(Q$_{m}$) and Curie temperature(T$_{c}$) of 0.1 wt% MnO$_2$ added specimen showed the optimal values of 7.75 g/㎤, 1503, 0.57, 1502, and 337, respectively, for multilayer piezoelectric transformer application.ation.n.