High-temperature Superconductor(HTS) tubes were fabricated in term of different processing variables such as preheating temperature, speed of mold rotation and cooling rate by centrigugal forming method. For powder melting by induction the optimum range of melting temperatures and preheating temperature were $1050{circ}C{sim}1100{circ}C;and;550{circ}C;for;30; min$, respectively The mould roating speed was 1000 rpm. A tube was annealed at $840 {circ}C$ for 72 hours in oxygen atmosphere. The plate-like grains were well developed along the loafing direction and typical grain size was about more than $40{mu}$. It was found that Ic values increased with increasing the Preheating temperature and speed of mold rotation. While Ic decreased with increasing the cooling rate. The measured Ic in $50mm{ imes}70mm{ imes}2.5mm$ tube was about 896 Amp.