The rutile polycrystal $Ti_{0.99};^{57}Fe_{0.01}O_2$ prepared with $^{57}Fe$ enriched iron have been studied by $Mddot{o}ssbauer$ spectroscopy, X-ray diffraction and VSM. The $Mddot{o}ssbauer$ spectrum of $Ti_{0.99};^{57}Fe_{0.01}O_2$ consists of a ferromagnetic and a paramagnetic phase over all temperature ranging from 4 to 300 K. Isomer shifts indicate $Fe^{2+}$ for the ferromagnetic phase, but $Fe^{3+}$ for the paramagneic phase of $Ti_{0.99};^{57}Fe_{0.01}O_2$ sample. It is noted that the magnetic hyperfine field of ferromagnetic phase had the value about 1.48 times as large as that of $alpha$-Fe. The XRD data for $Ti_{0.99};^{57}Fe_{0.01}O_2$ showed a pure rutile phase with tetragonal structures without any segregation of Fe into particulates within the instrumental resolution limit The magnetic hysteresis (M-H) curve at room temperature showed an obvious ferromagnetic behavior and the magnetic moment per Fe atom under the applied field of 1 T was estimated to be about $0.71{mu}_B$, suggesting a low spin configuration of Fe ions.