The effect of pH on the corrosion characteristics in the dissimilar friction welded zone of IN713LC-SCM440 in the loaded torsional stress was studied. The corrosion experiment was performed for 120 hours on the specimens with five steps of pH. The surface corrosion pattern of the SCM440 area showed global corrosion and narrow pitting, which was caused by galvanic corrosion between friction welded IN713LC and SCM440, but corrosion did not proceeded from the IN713LC area. The average relative electrode potential gradually tends to decrease with the elapse of the immersion time in the acidity area. The average corrosion current also gradually tend to decrease The corrosion rate showed a larger value when the average relative electrode potential was higher and the average relative current was lower. The corrosion rate showed a larger value when the average relative electrode potential was higher in the acidity area, and it showed large when the average relative electrode potential was lower in the alkalinity area.