[ $Li_3AlH_6$ ] (5.6wt% theoretical hydrogen storage capacity) powders with and without Ti-containing dopants have been successfully synthesized by mechanochemical reaction near room temperatures from mixtures of LiH and $LiAlH_4$ powders. It has been observed that single phase $Li_3AlH_6$ could be obtained within 2-3 hours of milling, but the addition of reactive $TiCl_2;or;TiCl_3$ to the starting mixtures. caused partial decomposition of $LiAlH_4$ into LiCl and free Al with gaseous $H_2$. By addition of these reactive dopants to the as-synthesized $Li_3AlH_6$, this problem could be solved. The addition of 2 mol% $TiCl_2;or;TiCl_3;to;Li_3AlH_6$ decreased the decomposition start temperature up to 30-50$^{circ}C$, while that of Ti or $TiH_2$ did not change the thermal decomposition behavior of $Li_3AIH_6$.