Many researchers have been focused on polymer electrolyte membrane (PEM) to improve performance of a fuel cell. Sulfonpolyimide with hydrocarbon was synthesized from ODA (4,4-diaminodiphenyl ether), ODADS (4,4-diaminodiphenyl ether-2,2-disulfonic acid), NTDA (1,4,5,8-naphthalenetetracarboxylicdianhydride) and CSA (chlorosulfonic acid). In order to estimate the feasibility as a fuel cell, the performance of sulfonpolyimide was analyzed through a swelling degree, IEC (ion exchange capacity), ion conductivity and TEM (transmission electron microscope). As the results of this performance test, swelling degree, IEC and ion conductivity were 37%, 0.06 meq/g and 0.08 S/cm respectively, when the CSA concentration was 0.4 M. It was thought that sulfonpolyimide could be used as a fuel cell through improvement of electrolyte membrane.